inCoris TZI C - Pre-shaded translucent zirconium oxide sinter ceramic for fabrication of bridges and crowns

Advantages:

Classic colors A-D

Can be used in the production of full anatomical restorations, which can be polished or veneered after milling and sintering

Very good aesthetic properties

Increased hardness

Good biocompatibility

Chemical composition:

ZrO₂+HfO₂+Y₂O₃: ≥ 99.0%

Y₂O₃: 5.6% (Σ Y₂O₃ + Er₂O₃)

Al₂O₃: ≤ 0.35%

Other oxides (except Er₂O₃): ≤ 0.2%

Technical Data (applicable to sintered material in HTC inFire HTC / inFire HTC speed):

Density: 6.08 g cm^-3

Fracture resistance KIC: 6.4 MPa m^1/2

Thermal expansion coefficent (20 - 500 °C): 11 10^-6 K^-1

Bending resistance: > 900 MPa

Dimensions: medi S (L x W x H): 40 x 19 x 15.5 mm

Indications:

Full anatomical crowns and bridges in the anterior and posterior areas

Bridges with up to nine units and maximum 2 pontics

Contraindications:

Insufficient oral hygiene

Insufficient tooth structure

Insufficient space available

Insufficient preparation results

Delivery form:

inCoris TZI C medi S - 1 x 3 blocks