inCoris TZI C - Pre-shaded translucent zirconium oxide sinter ceramic for fabrication of bridges and crowns

Advantages:

Classic colors A-D

Can be used in the production of full anatomical restorations, which can be polished or veneered after milling and sintering

Very good aesthetic properties

Increased hardness

Good biocompatibility

Chemical composition

ZrO2+HfO2+Y2O3: ≥ 99.0%

Y2O3: 5.6% (Σ Y2O3 + Er2O3)

Al2O3: ≤ 0.35%

Other oxides (except Er2O3): ≤ 0.2%

Technical Data (applicable to sintered material in HTC inFire HTC / inFire HTC speed):

Density: 6.08 g cm-3

Fracture resistance KIC: 6.4 MPa m1/2

Thermal expansion coefficent (20 - 500 °C): 11 10-6 K-1

Bending resistance: > 900 MPa

Dimensions: maxi M (L x W x H): 65 x 40 x 22 mm

Indications:

Full anatomical crowns and bridges in the anterior and posterior areas

Bridges with up to nine units and maximum 2 pontics

Contraindications:

Insufficient oral hygiene

Insufficient tooth structure

Insufficient space available

Insufficient preparation results

Delivery form:

inCoris TZI C maxi M - 1 block