SYSTEM NH is easy to use and quick to polish with excellent laser welding properties. The alloy can be melted by open flame or induction heating.

Adentatec System NH

<p></p>
<h1>SYSTEM NH</h1>
<p><b>SYSTEM NH is a non-precious dental cast alloy for crowns and bridges on nickel-base, type 4</b></p>
<p>SYSTEM NH is easy to use and quick to polish with excellent laser welding properties. The alloy can be melted by open flame or induction heating.</p>
<p>SYSTEM NH can be used with any commercial, phosphate-bonded investment material (our recommendation: ADENTA®-VEST CB).</p>
<p>SYSTEM NH can be veneered with any high-fusing ceramics.</p>
<h2>TYPICAL MATERIAL PROPERTIES</h2>
<figure><table><tbody><tr><td>Yield strength 0,2 % (MPa)</td><td>380</td></tr><tr><td>Elongation (%)</td><td>9,0</td></tr><tr><td>E-Module (GPa)</td><td>175</td></tr><tr><td>Tensile strength (MPa)</td><td>580</td></tr><tr><td>Density (g/cm³)</td><td>8,2</td></tr><tr><td>Corrosion resistance (µg/cm²)</td><td>&lt; 200</td></tr><tr><td>Melting range (Solidus/Liquidus) (°C)</td><td>1280 / 1340</td></tr><tr><td>Casting temperature (°C)</td><td>1430</td></tr><tr><td>Hardness&nbsp; HV 10/30</td><td>240</td></tr><tr><td>CTE (25-500°C) (10-6K-1)</td><td><b>~</b>14,0</td></tr><tr><td>Max. firing temperature (°C)</td><td><b>~</b>980</td></tr><tr><td>Delivery form (mm)</td><td>Ø 9,5 x 11</td></tr><tr><td>Packaging unit (g)</td><td>1000 g</td></tr><tr><td>Type acc. DIN EN ISO 22674:2016</td><td>≥ Type 4 as delivered</td></tr></tbody></table></figure>
<p>Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.</p>
<h2>TYPICAL COMPOSITION<figure><table><tbody><tr><td>Ni</td><td>Cr</td><td>Mo</td><td>Si</td><td>no other
elements</td></tr><tr><td>58,0</td><td>27,3</td><td>12,8</td><td>1,7</td><td>&gt; 0,1</td></tr></tbody></table></figure>
</h2>

Yield strength 0,2 % (MPa)	380
Elongation (%)	9,0
E-Module (GPa)	175
Tensile strength (MPa)	580
Density (g/cm³)	8,2
Corrosion resistance (µg/cm²)	< 200
Melting range (Solidus/Liquidus) (°C)	1280 / 1340
Casting temperature (°C)	1430
Hardness HV 10/30	240
CTE (25-500°C) (10-6K-1)	~14,0
Max. firing temperature (°C)	~980
Delivery form (mm)	Ø 9,5 x 11
Packaging unit (g)	1000 g
Type acc. DIN EN ISO 22674:2016	≥ Type 4 as delivered

Ni	Cr	Mo	Si	no other elements
58,0	27,3	12,8	1,7	> 0,1

Adentatec System NH

SYSTEM NH

TYPICAL MATERIAL PROPERTIES

TYPICAL COMPOSITIONNiCrMoSino other elements58,027,312,81,7> 0,1

TYPICAL COMPOSITION
Ni Cr Mo Si no other elements
58,0 27,3 12,8 1,7 > 0,1